Abstract
Metal-doped iron silicides (β-FeSi2) are promising thermoelectric materials for high-temperature applications. However, the addition of metal dopants usually causes the formation of secondary metallic phases, resulting in the degradation of thermopower. Here we report the stability of semiconducting β-phase (higher than 95 %) of Mn-doped β-FeSi2 obtained at Mn concentration from 1 % to 5 %, where the samples were prepared through direct arc melting and heat treatment process. The carrier density remarkably increases with Mn content, but the mobility decreases. The electrical resistivity significantly decreases with Mn content. The Seebeck coefficient of Mn-doped samples is improved and stable at high-temperature regions because of the reduction of the bipolar effect and β-phase stability. The thermal conductivity slightly increases with Mn. As a result, the maximum thermoelectric power factor PF = 970 μWm−1K−2 and dimensionless figure of merit ZT = 0.12 at 800 K are obtained in a 3 % Mn-doped sample. The stability of β-phase and the improved carrier density are the origins of enhanced thermoelectric properties, where the Seebeck coefficient is improved, and the electrical resistivity is reduced. Our study provides insight into the importance of phase stability for enhancing thermoelectric transport in Mn-doped β-FeSi2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.