Abstract
Sttess relaxation of bent beam specimens under fast neutron irradiation at 340 and 570 K has been studied for a range of materials, as follows: several stainless steels, a maraged steel, AISI4140, Ni, Inconel X-750, Ti, Zircaloy-2, Zr-2.5% Nb and Zr 3 Al. All specimens were in the annealed or solution-treated condition. Where comparisons were possible, the creep coefficients derived from the stress relaxation tests were found to be consistent with other studies of irradiation-induced creep. The steels showed the lowest rates of stress relaxation; the largest rates were observed with Zr-Nb, Ti and Ni. For most materials, the creep coefficient at 340 K was equal to or greater than that at 570 K. Such weak temperature dependence is not easily reconciled with existing models of irradiation creep based on dislocation climb, such as SIPA or climb-induced glide. Rate theory calculations indicate that because the vacancy mobility becomes very low at the lower temperature, recombination should dominate point defect annealing, resulting in a very low creep rate compared to that at the higher temperature. It is shown that the weak temperature dependence observed experimentally cannot be accounted for by the inclusion of more mobile divacancies in the calculation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.