Abstract
Injectable and biodegradable alginate-based composite gel scaffolds doubly integrated with hydroxyapatite (HAp) and gelatin microspheres (GMs) were cross-linked via in situ release of calcium cations. As triggers of calcium cations, CaCO3 and glucono-d-lactone (GDL) were fixed as a mass ratio of 1:1 to control pH value ranging from 6.8 to 7.2 during gelation. Synchronously, tetracycline hydrochloride (TH) was encapsulated into GMs to enhance bioactivity of composite gel scaffolds. The effects of HAp and GMs on characteristics of gel scaffolds, including pH value, gelation time, mechanical properties, swelling ratio, degradation behavior and drug release, were investigated. The results showed that HAp and GMs successfully improved mechanical properties of gel scaffolds at strain from 0.1 to 0.5, which stabilized the gel network and decreased weight loss, as well as swelling ratio and gelation time. TH could be released from this composite gel scaffold into the local microenvironment in a controlled fashion by the organic/inorganic hybrid of hydrogel network. Our results demonstrate that the HAp and GMs doubly integrated alginate-based gel scaffolds, especially the one with 6% (w/v) HAp and 5% (w/v) GMs, have suitable physical performance and bioactive properties, thus provide a potential opportunity to be used for bone tissue engineering. The potential application of this gel scaffold in bone tissue engineering was confirmed by encapsulation behavior of osteoblasts. In combination with TH, the gel scaffold exhibited beneficial effects on osteoblast activity, which suggested a promising future for local treatment of pathologies involving bone loss.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.