Abstract
The inhomogeneous microstructure and fatigue crack propagation of 30 mm thick-section high strength steel welded joint by double-sided hybrid fiber laser-arc welding were investigated in detail. The results indicated that the average effective grain size of the laser zone was only 1/2 of that of the arc zone, due to the faster cooling rate of the laser resource. The base metal consisted of massive polygonal ferrites and small granular carbides, while fine grained region, the coarse grained region and weld metal were all composed of martensite with a high dislocation density. Compared with the arc zone, the percentage of grain boundaries with high misorientation angle increased 24% for the laser zone, as the average grain size of the laser zone was smaller than that of the arc zone. The results also revealed that the fatigue crack propagation resistance of the welded joint was higher than that of the base metal. Meanwhile, a significant increase in the fatigue crack propagation resistance of the laser zone occurred, as compared with the arc zone, due to the refined grains and the high proportion of the grain boundaries with high misorientation angle (>15°) in the laser zone.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call