Inhomogeneous grain growth and elongation of Dy-α sialon ceramics at temperatures above 1800°C

Abstract

A series of samples with dysprosium α-sialon compositions and different amounts of sintering additives has been fabricated from α-Si 3N 4, AlN, Al 2O3 and Dy 2O 3 starting powders, using pressureless sintering (PLS) at 1800°C plus gas pressure sintering (GPS) at the same and higher temperatures under a relatively low gas pressure of 0.9 MPa N 2. The resultant α-sialon grains show significantly different features, such as regularly fine and equiaxed, elongated, and even a few extraordinarily large with high aspect ratio grains in the fine matrix, which has rarely been observed in α′ ceramics. It is suggested that the temperature strongly influences the grain morphologies of α-sialon, playing an important role particularly in the latter stage of the “nucleation-growth” process. Such a kind of microstructural morphology as mixed with equiaxed and elongated grains toughens the α-sialon ceramics and leaves them still hard as usual. Overly high temperature treatment leads to the preferential growth of a few grains which become excessively large and long, and do not significantly improve the materials toughness.