Inhibition of Sulphuric Acid Corrosion of Mild Steel by Surfactant and Its Adsorption and Kinetic Characteristics

Abstract

The corrosion inhibition effect of surfactant, N,N-Dimethyl-N-(2-Phenoxyethyl)dodecan-1- aminiumbromide(DPDAB) on mild steel corrosion in 0.5M Sulphuric acid was investigated by weight loss, potentiodynamic polarization and Electrochemical impedance spectroscopic techniques. DPDAB is an excellent inhibitor and its inhibition efficiency increases with increase in concentration and maximum inhibition efficiency was observed above the critical micelle concentration (CMC). The polarization curves reveal that DPDAB acts as mixed type inhibitor with predominantly of anodic type. The corrosion inhibition efficiency of DPDAB increases with increase in concentration and decreases with increase in temperature from 298K to 308K and then increases and shows maxima at 318K and then decreases at 328K.. The adsorption of the inhibitor on the mild steel in 0.5M H2SO4 was found to obey Langmuir's adsorption isotherm. Scanning electronic microscopy (SEM) confirmed the existence of an adsorbed protective film on the metal surface. The kinetic and thermodynamic parameters were calculated and discussed.