Abstract
The microstructural evolution of infrared brazed joint is primarily depended upon redistribution of alloying elements such as Cu, Ni and Nb across the joint. For the specimen infrared brazed at 970 °C for 180 s, the joint primarily consists of coarse eutectic Ti 2Cu, Ti 2Ni intermetallics and transformed β-Ti. Increasing the brazing time to 600 s results in a fine eutectoid microstructure dominating the entire joint due to the depletion of Cu and Ni from the braze alloy into Ti–6Al–4V substrate. Ti 2Cu, Ti 2Ni and transformed β phases are almost absent from the specimen infrared brazed for 3600 s, and the β-Ti is stabilized by alloying high concentration of Nb. Based on the shear test result, all cracks propagate along the Nb substrate with typical ductile dimple rupture appearance. Consequently, Ti–6Al–4V and Nb can be vacuum brazed by Ti–15Cu–15Ni foil with good joint strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.