Abstract
Various surface platinized TiO 2 were prepared by four different preparation methods and investigated with respect to their behaviors in UV photocatalytic oxidation of nitric oxide. The physicochemical properties of the Pt modified TiO 2 were investigated by X-ray diffraction analysis, X-ray photoelectron spectrum analysis, transmission electron microscopy, and photoluminescence spectra. From the experimental results, it was found that new electronic states were observed above the valence bands of PtOx-TiO 2 and PtClx-TiO 2. And the lifetime of electrons and holes was found prolonged in the PtOx-TiO 2 catalysts. The activity tests showed that the dopants existed as metallic Pt and platinum chloride had little contribution to the photocatalytic oxidation of NO in gas phase. However, the dopant which existed as PtOx could improve the NO photocatalytic oxidation efficiency and the reaction rate. The photocatalytic activity of the 0.05 at% PtOx-TiO 2 was nearly three times higher than that of the pure Degussa P25 with an inlet NO concentration of 200 ppm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.