Abstract
A356.2 aluminum alloy (Al–7Si–0.35Mg) has been widely used in automotive and aircraft industries. Previous studies found that the metamorphism effect of rare earth is better than other type of elements because of long modification time and good stability. The influence of Yb addition (0%, 0.2%, 0.4% and 0.6%) and T6 heat treatment on A356.2 alloy has been investigated in this work. The microstructures and mechanical properties of the specimen after T6 treatment were examined by optical microscope, scanning electronic microscope and tensile tests. Experimental results showed that Yb could reduce the size of α-Al and change the Si morphology from needle-like to fine spheroidal particles. With the increase of Yb content, the ultimate tensile strength increased gradually. When adding 0.4%Yb, the alloy achieved the highest ultimate tensile strength (252 MPa) and hardness (97.3HB), 10.12% and 37.66% higher than the alloy with no Yb addition. Tensile fracture analysis showed that the fracture mechanism for A356.2 aluminum alloy after T6 treatment is transgranular/intergranular mixed mode of fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.