Influence of Y Content and T6 Heat Treatment on the Organization and Mechanical Properties of Cast A356 Aluminum Alloy

Abstract

The effect of Y content on the microstructure of A356 aluminum alloy and the mechanical properties of the alloy under T6 heat treatment was investigated. The results show that with the addition of 0.3 wt.% rare earth Y, the grain size of the cast A356 aluminum alloy reaches a minimum and the mechanical properties reach an optimum. After the T6 heat treatment, the grain structure of the alloy was further reduced and the mechanical properties were further improved. Compared to the cast A356 aluminum alloy without Y, the average α-Al grain size is reduced by 53.4%, the secondary dendrite SDAS by 32.2% and the average length of eutectic Si particles by 82.0%. The ultimate tensile strength (UTS) and elongation (El) increased to 280.75 MPa and 14.43% respectively, and the Vickers hardness increased to 102.9 HV.