Abstract
Pineapple fiber reinforced polyvinyl chloride (PVC) composites (25-75% fiber by weight) were fabricated using compression molding technique and the mechanical properties such as tensile strength (TS), tensile modulus (TM), bending strength (BS), bending modulus (BM) and impact strength (IS) of the composites were evaluated. It was found that at 55% fiber content, the composite exhibited the best mechanical properties. The TS, TM, BS, BM and IS were found to be 48.8 MPa, 773 MPa, 75.6 MPa, 4.2 GPa, 21.4 KJ/m2 for 55% fiber composite. The composites were exposed to different intensities of ultraviolet (UV) radiation (25-200 UV dose) and found significant improvement in the mechanical properties up to 100 UV dose. At 100 UV dose, the value of TS, TM, BS, BM and IS of the composite were found to be 57.3 MPa, 932 MPa, 87.5 MPa, 5.2 GPa and 26.3 KJ/m2 respectively. Water uptake behaviours of the non-irradiated and UV irradiated composites were also observed. The interfacial property was examined by scanning electron microscopy (SEM).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.