Abstract
In the current research work synthesis, characterization, mechanical and wear behavior of 2, 4 and 6 wt% of nano-ZrO2 particulate-reinforced AA2014 alloy composites have been investigated. The matrix phase of AA2014 alloy containing nano-ZrO2 particulates composites was geared up by two-stage melt stir system. After the preparation, the organized composites were studied by SEM and EDS for analyzing the microstructures and chemical elements. Further, mechanical characterization and wear studies of as-cast AA2014 alloy and AA2014-nano-ZrO2 composites were studied. From the investigation, it was observed that the tensile behavior of composites was enhanced due to addition of nano-sized ZrO2 particles in the AA2014 alloy matrix. In nano-ZrO2-reinforced composites, the percentage elongation decreased. Further, the wear loss increased with respect to the load for all the prepared materials. To study the fractography and different wear mechanisms for various test conditions of different compositions, tensile fractured surfaces and the worn surfaces were observed by SEM.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.