Abstract
The effects of tungsten doping in La2Mo2–yWyO9 (y =0, 0.25, 0.5, 1.0, 1.4) samples were studied using dielectric relaxation measurements. The results indicate that the solubility of W6+ in La2Mo2O9 sample is about 25mol%, W6+ can suppress the α/β phase transition in the La2Mo2O9. Additional to the low-temperature relaxation peak Pd associated with oxygen ion diffusion, a new dielectric loss peak Ph associated with a phase transition from the static disordered state to the dynamic disordered state of oxygen ion distribution was observed around 740 K. The conductivity of La2Mo1.9W0.1O9 sample is higher than that of the pure La2Mo2O9, and then decrease with the increasing of the tungsten doping in La2Mo2–yWyO9 (y = 0.5, 1.0) samples in the whole measurement temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.