Abstract
This study examines dissimilar friction stir welding of AA5052-AA6061 aluminum alloys with varying tool offsets. The base metals were positioned and fixed at a slight diagonal positioning such that varying tool offset position from the centreline can also be varied along the length of the weld. After the fabrication process, microstructural and mechanical property characterization was subsequently conducted. The results show that, above a certain threshold for tool offset, incomplete consolidation (i.e. kissing bond defects) will occur. Regardless of the base material positioning, a zero tool offset shows optimum intermixing in the stir zone. EDX mapping confirms the presence of a distinct interface between both materials in the stir zone region. However, enhanced material intermixing and better elongation are observed when AA6061 alloy is positioned at the tool advancing side.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.