Abstract
In the current study, the influence of TiO2/SiO2 and BaO/CaO ratios on viscosity, crystallization and structure of high-TiO2 mold slags was discussed through the measurement of viscosity-temperature relationship, melting temperature, crystallization temperature, crystallization rate and phases, and Raman spectrum. With the substitution of SiO2 by TiO2 in slags from 0 % to 12 %, the viscosity at 1300 °C, the melting temperature and break temperature decreased and then increased, while those of slags with the substitution of CaO by BaO from 4 % to 16 % decreased. With the substitution of SiO2 by TiO2 from 0 % to 10 %, crystallization phases gradually changed from cuspidine (Ca4Si2F2O7) to perovskite (CaTiO3), the initial and complete crystallization temperatures had the tendency to increase from 918 °C to 1260 °C and from 857 °C to 1139 °C, respectively, and the overall crystallization ability of slags increased. With the substitution of CaO by BaO from 4 % to 16 %, the initial and complete crystallization temperature of these slags decreased, and the overall crystalline ability decreased. With the substitution of SiO2 by TiO2 from 0 % to 10 %, structural units changed from the simple units to complex units, but the transition was opposite with the substitution from 10 % to 12 %, which was related to the transition of TiO2 from basic oxide to amphoteric oxide. With the substitution of CaO by BaO from 4 % to 16 %, the degree of polymerization and the viscosity of theses slags decreased, which was related to the supplement of more active O2− ion from BaO. Hence, the excessive substitution of SiO2 by TiO2 under the steel-slag reaction would cause the increase of the slag viscosity and crystallization ability, while the substitution of CaO by BaO could weaken the variation of slag viscosity and crystallization ability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.