Abstract
Vanadium carbide (VC)-reinforced Fe-based hard facings are pivotal in enhancing the wear resistance of tools prone to mechanical damage. This study investigates the impact of titanium diboride (TiB2) addition (at varying laser power and powder federate) on the microstructure, hardness, wear resistance, and corrosion resistance of high-carbon ferrochrome FeCrV15 clad coatings for agricultural and mining applications. Laser cladding techniques were employed to deposit coatings on steel substrates, and the samples were subjected to comprehensive material characterization, including microhardness testing, wear studies, and electrochemical polarization. Results reveal that TiB2 addition led to visible reactions during deposition, resulting in decreased hardness compared to pure FeCrV15 coatings. Moreover, TiB2 incorporation adversely affected the anti-corrosion properties of the coatings, although FeCrV15 coatings exhibited superior corrosion resistance compared to FeCrV15 + TiB2 coatings. Tribological evaluations showed that all coatings exhibited better anti-wear capabilities compared to the steel substrate, with varying degrees of improvement influenced by TiB2 concentration and laser beam power. Overall, FeCrV15 deposits demonstrated superior anti-wear and anti-corrosion properties compared to FeCrV15 + TiB2 coatings and attributed to increased convergence of carbide particles and higher grain-boundary density. This research contributes to understanding the intricate interplay between carbide reinforcement and matrix structure in Fe-based hard facings, providing insights for optimizing coating performance in demanding industrial applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.