Influence of thermal treatment temperature on high-performance varistors prepared by hot-dipping tin oxide thin films in Nb2O5 powder

Abstract

SnOx-Nb2O5 thin film varistors were prepared by hot-dipping oxygen-deficient tin oxide films in Nb2O5 powder in air, and the influence of hot-dipping temperature (HDT) on the varistor performance of the samples was systematically explored. When the HDT increased from 300 to 700 °C, the nonlinear coefficient of the samples raised first and then dropped down, reaching the maximum of 14.73 at 500 °C, and the breakdown electric field exhibited a similar variation trend, gaining the peak value of 0.0201 V/nm at this temperature. Correspondingly, the leakage current decreased first and then increased with increasing HDT, reaching the minimum of 17.1 mA/cm2 at 500 °C. Besides, it was proposed that a grain-boundary defect barrier model was responsible for the nonlinear behavior of the obtained SnOx-Nb2O5 film varistors. This high-performance thin film varistor with nanoscaled thickness might be much promising in nano-devices or devices working in low voltage.