Abstract
ABSTRACTThe phase stability of C-22 alloy (UNS N06022) gas tungsten arc welds was studied by aging samples at 593, 649, 704, and 760°C for times up to 6,000 hours. The tensile properties and the Charpy impact toughness of these samples were measured in the as-welded condition as well as after aging. The corrosion resistance was measured using standard immersion tests in acidic ferric sulfate (ASTM G 28 A) and 2.5% hydrochloric acid solutions at the boiling point. The microstructures of weld samples were examined using scanning electron microscopy (SEM). Precipitate volume fraction measurements were made using optical microscopy.Degradation of the mechanical and corrosion properties of C-22 welds due to aging at all temperatures investigated was seen to occur sooner than was seen in C-22 base metal. An evaluation of the kinetics of nucleation and growth of the precipitates forming at these temperatures, however, indicated that no significant changes in TCP phase morphology would occur at temperatures below approximately 300°C.a
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.