Abstract
In this study, natural rubber (NR) was treated with sulfuric acid to improve its adhesion properties to polar polymer. T-peel strength tests, scanning electron microscopy, contact-angle measurement (water), Energy Dispersive X-ray Detector were used to analyze the nature of the NR surface modifications which were carried out with sulfuric acid. A noticeable decrease in contact angle was observed on the rubber surface by contact-angle measurements which can be ascribed to the increase of oxidized moieties on the rubber surface. EDX revealed that oxidized moieties were created through treatment with sulfuric acid. The surface modification and mode of bond failure were studied by scanning electron microscopy (SEM). Immersion in sulfuric acid for 15min produced the maximum adhesion strength (10kN/m) and produced a mixed failure mode (interface & rubber failure in the rubber). Treatment with sulfuric acid produced improved wettability as well as chemical (surface oxidation) and morphological modifications (roughness) of the rubber surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.