Abstract
A novel partway for the fabrication of copper-indium (gallium) diselenide has been developed. This two-stage process consists of the formation of Cu-In-(Ga)-Se precursors and subsequent selenization to form CuIn(Ga)Se2. In this work, we have investigated and compared the possible interactions in Cu-In-Ga-Se systems, using sequentially stacked precursors premixed with Se, in order to get a better understanding of the Cu(In,Ga)Se2 thin film formation. Comparison of these SEM micrographs clearly revealed that the surface morphologies and hence surface roughness of the resulting Cu(In,Ga)Se2 absorber films were significantly influenced by the structure of the precursor films prior to selenization. XRD analyses revealed the presence of a graded CuIn1-xGaxSe structure, irrespective of the stacking order during the precursor formation step for samples selenized using elemental Se vapor. It was established that distinct from the case of using Se vapor, a single-phase Cu(In,Ga)Se2 films were obtained by diethylselenide (DESe) selenization from Cu-In-Ga metal precursors premixed Se irrespective of the stacking order during the precursor formation step. (© 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.