Abstract
This study evaluated the influence of the resin composite and bonding strategy on the push-out bond strength of the self-adhesive, Fusio liquid dentin (FUS) (Pentron Clinical), and of two conventional resin composites of different viscosities, Filtek Z250 (3M ESPE) and tetric flow (Ivoclar Vivadent). Thirty-two bovine incisors were used after disinfection. The roots were sectioned and the buccal and lingual surfaces were polished until a 2-mm slab was achieved, maintaining enamel at the buccal surface and dentin at the lingual surface. Standardized cavities were then prepared (2.0 × 1.5 mm) and restored according to the following bonding strategies: Fusio liquid dentin with selective etching (FUSSE) in enamel, FUS, Filtek Z250, and tetric flow-total etching (TET). All groups were restored in bulk. After 24 hours of storage in distilled water, finishing and polishing were performed. The push-out test was conducted on a universal testing machine (0.05 mm/minute). Data were analyzed through Kruskal-Wallis and Mann-Whitney tests (p = 0.05). The extruded restorations were evaluated under a stereomicroscope (10×) for failure-mode evaluation. There were no statistically significant differences between the groups TET, Z250, and FUS, with 145.59, 108.91, and 104.12 MPa means, respectively. The FUSSE group (40.92 MPa) showed a statistically significant lower bond strength. The predominant failure mode was a mixed failure for all groups. The self-adhesive resin composite achieved a satisfactory result on bond strength when compared to conventional composites with regular and low viscosities, except when selective enamel etching was done. This study shows that the clinicians must be aware of the viscosity of the phosphoric acid to avoid dentin contamination whenever performing selective enamel etching. And the self-adhesive resin composite studied presented as another restorative alternative.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.