Abstract
This study evaluated the effects of curing modes and storage conditions on fluoride release of resin cements. In phase 1, the cumulative fluoride release rate from samples of the resin cements (Panavia F 2.0, RelyX Unicem, MaxCem, and BisCem) was quantified after 15 days storage in water (n=4). In phase 2, the fluoride release profiles from the same materials were analyzed during pH cycling (n=4). In this second phase, fluoride was measured at specific times (one, two, three, five, eight, and 15 days). Disk-shaped specimens were prepared (10 mm × 0.5 mm), and the materials were either light activated or allowed to autopolymerize. For both phases, the fluoride release was measured using a fluoride ion-specific electrode. The fluoride release in water was not affected by the curing mode of RelyX Unicem and Maxcem resin cements. Panavia F. 2.0 and BisCem resin cements, either light cured or autopolymerized modes, released higher amounts of fluoride in water than the other self-adhesive cements. In phase 2, the concentration of fluoride released decreased from the first day of pH cycling until the 15th day for all resin cements, for both curing modes, regardless of the storage solution used (demineralizing/remineralizing). The fluoride release rate during pH cycling by Panavia F 2.0 and MaxCem was not affected by the curing mode. The effect of the curing mode on fluoride ion release in water or during pH cycling was product dependent.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.