Abstract
The influence of 200 keV Ar-ion irradiation on the interlayer coupling in Fe/Cr multilayers exhibiting the giant magnetoresistance (GMR) effect is studied by the conversion electron Mössbauer spectroscopy (CEMS), vibrating sample magnetometer hysteresis loops, magnetoresistivity, and electric resistivity measurements and supplemented by the small-angle x-ray diffraction. The increase of Ar-ion dose causes an increase of interface roughness, as evidenced by the increase of the Fe step sites detected by CEMS. The modification of microstructure induces changes in magnetization reversal indicating a gradual loss of antiferromagnetic (AF) coupling correlated with the degradation of the GMR effect. Distinctly weaker degradation of AF coupling and the GMR effect observed for irradiated samples with a thicker Cr layer thickness suggest that observed effects are caused by pinholes creation. The measurements of temperature dependence of remanence magnetization confirm increase of pinhole density and sizes during implantation. Other effects which can influence spin dependent contribution to the resistance, such as interface roughness as well as shortening of mean-free path of conduction electrons, are also discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.