Abstract
High-cycle fatigue tests of compacted graphite iron (CGI) at 25 °C, 400 °C and 500 °C were performed. The corresponding fatigue damage mechanisms were investigated by the observations on fractographies and longitudinal section morphologies of typical samples. The results show that the decreasing rate of fatigue strength from 400 °C to 500 °C is higher than that from 25 °C to 400 °C. The fatigue strength coefficient of S-N curve fitted with the Basquin relationship decreases from 25 °C to 400 °C and increases from 400 °C to 500 °C; while the fatigue strength exponent performs in an inverse tendency. These are resulted from plastic deformation mode transition of the ferrite at the tip of the crack induced by the graphite debonding: slip band at 25 °C and 400 °C to grain boundary sliding at 500 °C. Finally, the influences of carbide on fatigue properties were discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.