Abstract
The effect of additives based on acicular calcium hydrosilicates (xonotlite and tobermorite) and wollastonite, obtained from boric acid production waste in autoclave synthesis at a temperature of 220 °C, on the strength of fine-grained concrete, has been studied in this paper. It was shown that when the calcium hydrosilicates and wollastonite are introduced, an increase in the strength characteristics of concrete is observed. After heat and moisture treatment, the maximum increase in strength is observed with the addition of 4% of mass content of calcium hydrosilicates and 6% of mass content of wollastonite. After 28 days of hardening under normal conditions, the maximum increase in strength of concrete is observed with the addition of 4% of mass content of both types of additives. It was shown that the water absorption of concrete decreases with a maximum when 4% of mass content is added, as in the case of the introduction of calcium hydrosilicates, and wollastonite. With a further increase in the number of additives, the amount of water absorption increases, but these values remain below the values for the control sample without additives.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.