Abstract
CHA-type zeolite membranes with excellent dehydration performance can be prepared on a porous α-Al 2O 3 support tube by the secondary growth of seeds in a synthesis gel containing strontium. The permeation flux and separation factor of the membrane were 2.89 kg m −2 h −1 and >100,000, respectively, for a 50 mol% ethanol solution at 313 K. In this work, the CHA-type zeolite membranes were prepared using the gel with different compositions to discuss the influences of the synthesis gel composition on the morphology, composition, and dehydration performance of the CHA-type zeolite membrane. As a result, the CHA-type zeolite membrane could be prepared in the gel with the following compositions: SiO 2/Al 2O 3 = 2–16; H 2O/SiO 2 = 65–250; H 2O/(K 2O + SrO) = 100–400; SrO/(K 2O + SrO) = 0.10–0.85. Furthermore, the CHA-type zeolite membrane was ion-exchanged with lithium, sodium, rubidium, and cesium ions, and the dehydration performances of the ion-exchanged membranes were also determined. Based on these results, the effect of strontium for the membrane preparation was discussed in this paper.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.