Abstract
The subject of the work was to study the effect of Ti thin film on alumina ceramic on mechanical strength and fracture character of Al2O3/Al/Al2O3 joints. The joints were formed by liquid state bonding of alumina substrates covered with titanium thin film of 800 nm thickness using Al interlayer of 30μm thickness at temperature of 973 K in a vacuum of 0.2 mPa for 5 min. The bend strength was measured by four–point bending test at room temperature. Scanning and transmission electron microscopy were applied for detailed characterization of interface structure and failure character of fractured joint surfaces.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.