Abstract
Liquid-phase epitaxial growth with higher supersaturated InP growth melt could be successfully used in fabricating InGaAsP/InP double heterostructure (DH) lasers emitting in the 1.50–1.55-μm wavelength region. InP-InGaAsP interface characterization has been carried out with scanning electron microscope (SEM), transmission electron microscope, photoluminescence (PL) measurements, and Auger spectroscopy. From the dissolution depth measurements, it was found that there is a slight dissolution on the surface of the InGaAsP layer, even in the 1.3-μm wavelength region during an InP layer growth with 16° supersaturated melt. Although the amount of dissolution increases as the composition of the quaternary active layer becomes a longer wavelength, as a result of this dissolution, the transition region does not catastrophically affect the laser performances at a wavelength shorter than 1.55 μm. It was found that the InP-InGaAsP interface at 1.59-μm wavelength shows rugged configuration under high-resolution SEM observation and the half-width of PL spectrum becomes wider than that for DH wafers at a wavelength shorter than 1.55 μm. This was confirmed by Auger line profile measurements.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.