The influence of superplasticizer (SP) on the early age drying shrinkage of cement paste with the same consistency was investigated. To conduct the test, which lasted for 72 hours, three paste mixtures were used for comparison. The 72 hours early age drying shrinkage staring from the initial setting time was measured by a clock gauge. The pore size distribution was measured by Mercury Intrusion Method. The surface tension of capillary simulation liquid and mass loss of paste were also measured. The experimental results showed that the addition of SP increased the early drying shrinkage greatly. The ratios of water evaporation and the total free water in mixtures added with SPs showed great differences. SPs fined the capillary pores of paste, and the volume of pore with diameter within 50 nm was well consistent with shrinkage rate. The addition of SPs did not raise the capillary liquid surface tension. It showed that with the volume of pore with diameter within 50 nm and the ratio of water evaporation and the total free water a tolerable shrinkage result of paste added with SP could be predicted, and the elastic modulus could have an influence on the early shrinkage. These results have never been proposed before.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.