Abstract
A low temperature sulfuric acid baking and mild acid leaching process was explored for maximum dissolution of metal values from a spent Ni–Mo/Al 2O 3 hydro-processing catalyst obtained from a Korean refinery. The spent catalyst was found to be a matrix of γ-Al 2O 3. containing 27.1% Al, 11.6% Mo, 2.5% Ni, 9.7% S, 4.8% C, 1.9% P, 0.4% Si and trace amounts of Co and Fe. Various baking parameters such as baking temperature, sulfuric acid concentration and baking duration were optimized according to 2 3 full factorial method for maximum dissolutions of Mo, Al and Ni during leaching. Under optimum baking conditions (400 °C; 1.28 stoichiometric H 2SO 4; 1 h), > 96% Mo, 99% Al and 95% Ni were readily dissolved from the spent catalyst by 2% v/v H 2SO 4 at 80 °C. Carbon and sulfur analyses of the baked samples and leaching residues indicated only 10–15% of residual hydrocarbons reacted during acid baking, while most of the sulfur (assumed to be metal sulfides) was converted into soluble sulfates/oxy-sulfates. By comparison, direct sulfuric acid leaching of the catalyst resulted in poor dissolution of Mo and Al, even with large excess of acid, thus demonstrating the beneficial effect of sulfuric acid baking.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.