Influence of sputtering conditions on the optical and electrical properties of laser-annealed and wet-etched room temperature sputtered ZnO:Al thin films

Abstract

We explore the influence of the sputtering deposition conditions on the outcome of an excimer laser anneal and chemical etching process with the goal of producing highly textured substrates for thin film silicon solar cells. Aluminum-doped zinc oxide (ZnO:Al) thin films were prepared on glass substrates by radio frequency magnetron sputtering from a ceramic target at room temperature. The effects of the process pressure (0.11–1.2Pa) and oxygen flow (0–2sccm) on the optical and electrical properties of ZnO:Al thin films have been studied both before and after an excimer laser annealing treatment followed by a dilute HCl chemical etch. The as-deposited films varied from completely opaque to yellowish. Thin film laser annealing dramatically improves the optical properties of the most opaque thin films. After laser annealing at the optimum fluence, the average transmittance in the visible wavelength range was around 80% for most films, and reasonable electrical performance was obtained for the films deposited at lower pressures and without oxygen flux (7Ω/□ for films of 1μm). After etching, all films displayed a dramatic improvement in haze, but only the low pressure, low oxygen films retained acceptable electrical properties (<11Ω/□).