Abstract
ABSTRACT In the present paper the influence of solution temperature 450–550°C on microstructure and mechanical properties of cast Al-12%-0.3% Mg and Al-16%-0.3% Mg alloys has been reported. It was observed that an increase in solution temperature increased the tensile strength of all alloys under investigation. Ductility was adversely affected. Higher solution temperature produced better refinement and distribution of eutectic silicon crystals than a low temperature. Heat treatment of all alloys showed spheroidization of eutectic silicon crystals. Scanning electron microscopy (SEM) of tensile-fractured surfaces was carried out to investigate the influence of solution temperature on the mode of fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.