Abstract
Abstract This study investigates the properties of sol-gel derived sodium (Na)-doped hydroxyapatite (HA) powder. Different amounts of Na (1, 5, 10 and 15 mol%) were prepared and the sintered bodies were characterized to determine the current phases, microstructural evolution and mechanical properties. X-ray diffraction analysis reveals that a phase pure HA of crystallite sizes, which varied from 35 nm to 65 nm, was obtained in the synthesized powder after calcining from 500 °C to 1000 °C. Scanning electron microscopy examination shows evidence of larger particle sizes, particularly in samples that contain higher amounts of Na concentration. The resultant powders were subsequently used to prepare porous NA-doped HA bodies through a polymeric sponge method. The addition of 5% Na resulted in a porous body with 27% porosity and was beneficial in enhancing the compressive strength of HA 17-fold compared with undoped HA. The prepared scaffold also shows suitable pore interconnectivity with pore sizes that vary between 100 and 300 µm which is suitable for use as porous bone substitutes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.