Abstract
The size and crystal orientation of Sn grains in Pb-free, near eutectic Sn-Ag-Cu solder joints were examined. A clear dependence of the thermomechanical fatigue response of these solder joints on Sn grain orientation was observed (Sn has a body centered tetragonal crystal structure). Fabricated joints tend to have three orientations in a cyclic twin relationship, but among the population of solder balls, this orientation triplet appears to be randomly oriented. In thermally cycled joints, solder balls with dominant Sn grains having the particular orientation with the c-axis nearly parallel to the plane of the substrate were observed to fail before neighboring balls with different orientations. This results from the fact that the coefficient of thermal expansion of Sn in the basal plane (along the alpha-axis) is half the value along the c-axis; joints observed to be damaged had the maximum coefficient of thermal expansion mismatch between solder and substrate at the joint interface, as well as a tensile stress modes during the hot part of the thermal cycle. Localized recrystallization was observed in regions of maximum strain caused by differential expansion conditions, and its connection with crack nucleation is discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IEEE Transactions on Components and Packaging Technologies
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.