Abstract
ZnO-modified (Li, Na, K)NbO3 lead-free ceramics with a nominal composition of Li0.06(Na0.535K0.48)0.94NbO3+0.7mol% ZnO (LNKN-Z7) was synthesized normally at 930–1000°C. The Zn ions incorporated into the A-site at a higher sintering temperature, which changed LNKN-Z7 to soft piezoelectric ceramics with the mechanical quality factor decreasing from 228 to 192. A phase transition from tetragonal to orthorhombic symmetry was identified by XRD analysis, and the corresponding calculation of lattice parameters was conducted at 970–980°C. Because of such transitional behavior and fine microstructure, the optimized values of piezoelectric coefficient, planar electromechanical coupling coefficient, and relative dielectric constant were obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.