Abstract
Gray iron, a widely used engineering material, is favored for its desirable properties such as good damping capacity, thermal conductivity, and corrosion resistance. However, when exposed to elevated temperatures over time, issues like oxidation and graphite depletion can impact its durability. High-silicon gray iron, with elevated silicon content exceeding 3.0%, is known for its ability to withstand heat and oxidation, making it suitable for many applications, including cookware. This study investigates the impact of varying silicon levels (2.00-4.56%Si) on the solidification behavior, microstructure, and oxidation resistance of gray iron. Three heats with different silicon concentrations were produced and analyzed. Results indicated that higher silicon content increases the eutectoid temperature, stabilizes the ferritic structure, and introduces Type-D graphite in the microstructure. Graphite depletion was observed only in samples with 2.00%Si. The oxidation resistance improved with higher silicon content, as evidenced by a decrease in weight gain after exposure to 800 °C for 4 hours. This suggests the potential of using lower silicon levels in gray iron for cookware applications, balancing material cost with good impact resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.