Abstract
ABSTRACT AA6082 matrix hybrid composites reinforced with different weight percentages (wt. %) of (SiC + Gr) ceramic particulates by conventional stir casting process is manufactured. The weight percentage of ceramic powder is varied from 4 wt. % to 12 wt. % in a stage of 4 wt. %. The microstructures, physical properties such as density and porosity, as well as mechanical properties like hardness and tensile strength of the fabricated hybrid composites, are analysed. The optical micrographs reveal the uniform distribution of (SiC + Gr) ceramic particulates in the aluminium matrix. Density and porosity of hybrid composite increases from 2.69 to 2.75 g/cm3 and 0.37% to 1.23% with increase in weight percentage of (SiC + Gr) ceramic particulates in the aluminium matrix from 0 wt. % to 12 wt. % respectively. Both the hardness and ultimate tensile strength have enhanced from 52 to 84 VHN and 163 to 189 MPa, respectively, with a reduction in percentage elongation from 8.6 to 5.2 with rise in weight percentage of (SiC + Gr) ceramic particulates in the aluminium matrix from 0 wt. % to 12 wt. %, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.