Abstract
TiB2 coatings with various Si doping levels were fabricated using magnetron sputtering from TiB2 and Si targets. The chemical and phase composition, microstructure, mechanical properties, and high-temperature oxidation resistance of the coatings were investigated using different techniques, such as electron probe microanalysis (EPMA), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), nanoindentation, and thermogravimetric analysis. The results revealed that the microstructure of the TiB2 coating with and without Si doping changed from an apparent columnar structure to a densely stacked structure, and finally to a nearly featureless planar structure. A certain amount of added Si limits the growth of TiB2 grains and favors the formation of a nanocomposite structure with nanocrystalline TiB2 grains embedded in an amorphous Si phase matrix, as shown by XPS and TEM results. The hardness reached a maximum value of 35.2 GPa at 4.5 at% Si and then linearly decreased upon further increasing the Si content, owing to the excessively amorphous phase in coatings. However, it is worth noting that the high-temperature oxidation resistance of the coatings was improved by Si addition, due to their compact homogeneous structure that hinders the diffusion of oxygen. The results indicate that the hardness and oxidation resistance of the coatings can be simultaneously improved by the addition of an appropriate Si content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.