Abstract
AbstractRing‐opening polymerization of L‐ or D‐lactide was realized at 140 °C for a period of 7 days in the presence of dihydroxyl poly(ethylene glycol) (PEG), with M̄n = 4000 g mol−1, using zinc lactate as initiator. The resulting poly(L‐lactide)–PEG–poly(L‐lactide) and poly(D‐lactide)–PEG–poly(D‐lactide) triblock copolymers are water soluble with polylactide (PLA) block length ranging from 11 to 17 units. Both the tube inverting method and rheological measurements were used to evaluate the gelation properties of aqueous solutions containing single copolymers or L/D copolymer pairs. Stereocomplexation between poly(L‐lactide) and poly(D‐lactide) blocks is observed for mixed solutions. Hydrogel formation is detected in the case of relatively long PLA blocks (DPPLA = 17), but not for copolymers with shorter PLA blocks (DPPLA = 11–13) due to partial racemization of L‐lactyl units. Racemization is largely reduced when the reaction time is shortened to 1 day. Under these conditions, DPPLA of 8 is sufficient for the stereocomplexation of PLA–PEG block copolymers, and DPPLA above 10 leads to the formation of hydrogels of PLA–PEG block copolymers. On the other hand, racemization appears as a general phenomenon in the (co)polymerization of L‐lactide with Zn(Lac)2 as initiator, although it is negligible or undetectable in the case of high molar mass polymers. Therefore, racemization is the limiting factor for the stereocomplexation‐induced gelation of water‐soluble PLA–PEG block copolymers where the PLA block length generally ranges from 10 to 30. Reaction conditions including initiator, time and temperature should be strictly controlled to minimize racemization. Copyright © 2010 Society of Chemical Industry
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.