Abstract
The pulsed magneto-oscillation (PMO) technique has the potential to be applied in the production of heavy steel ingot. In order to confirm it and achieve more insights, the solidification of rectangular 65Mn steel ingot with the size of 220 mm × 220 mm × 1000 mm was investigated under the impact of PMO. Experimental results present that PMO treatment can remarkably refine the solidified microstructure of 65Mn steel ingot in comparison with the reference ingot without PMO. The application of PMO not only significantly reduces the grain size, but also promotes the morphology transition of equiaxed grains from well-developed dendritic structures to globular structures. And the resulted globular morphology is mainly due to the fact that the PMO-induced forced flow enhances the stability of crystal growth. As a consequence, the average tensile strength of as-cast samples is enhanced from 643.4 to 762.9 MPa under the application of PMO.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.