Abstract
• Effect of proton irradiation on Nb-1Zr-0.1C alloy proposed for CHTR. • XRD line profile analyses of the data collected using synchrotron source. • Prediction of dislocation loop formation with XRDLPA and supported by TEM analysis. • Microstructure-mechanical property correlation by tensile and nanoindentation test. • Comparison of microstructure and mechanical properties with proton irradiated pure Nb . The microstructural evolution and corresponding changes in mechanical properties of proton irradiated Nb-1Zr-0.1C alloy have been studied as a function of irradiation dose. Different XRD line profile analyses (XRDLPA) have been carried out using synchrotron XRD data to evaluate the microstructural parameters. It is observed that coherent domain size decreases with an increasing microstrain within the domain as a function of dose. The dislocation density also increases and shows saturation at the highest dose. The Wilkens arrangement parameter decreases as a function of dose indicating the formation of correlated dislocations in the alloy matrix. Transmission electron microscopy (TEM) analysis confirms the presence of dislocation loops in the highest dose sample supporting the findings of XRDLPA. The strength and ductility of unirradiated and all irradiated samples have been evaluated as a function of dose. It is observed that the ductility reduces continuously along with increasing yield strength (YS) and ultimate tensile strength (UTS) as a function of dose. Nanoindentation was also carried out to measure the change in hardness of the alloy with dose. It is observed that the value of the nanohardness increases continuously from 1.74 GPa for the unirradiated sample to 2.43 GPa in the highest dose irradiated sample. Systematic changes are observed on the morphology of fracture surface as a function of dose. Signature of ductile failure is observed in the unirradiated sample whereas brittle failure is prominent in the irradiated samples with higher dose. The change in microstructure in terms of dislocation density is corroborated with the change in mechanical properties in terms of YS of the irradiated alloy. Contradistinction of the findings of Nb-1Zr-0.1C with those of pure Nb contemplated the role of the alloying additions, especially carbon, in governing the irradiation behaviour of the alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.