Abstract
AbstractSummary: Microcellular wood fibre reinforced polymer materials are significant because of their possibility to reduce the density of automotive components through microcellular structure, process and product part advantages, and as a new development with bio‐fibre strengthened plastics. Soft wood fibre reinforced PP composites in box part and panel shape were prepared by an injection moulding process. Polymeric microspheres as a chemical foaming agent (endothermic) were used to produce the microcellular composites. The influence of injection moulding processing temperature on the microcellular structure and properties (tensile and flexural properties, notched charpy impact strength) was investigated by varying the temperature over the 150–170 °C, 160–180 °C and 170–190 °C. A comparative study of cell morphology, weight reduction and mechanical properties was conducted between box part and panel. Microcell morphology, cell size, shape and distribution were investigated using scanning electron micrographs. The results indicated that the lower processing temperature should be below the range of 170–190 °C and processing temperature at 160–180 °C, where the composites showed finer cellular structure compared to other processing temperatures. The mechanical properties did not differ with the variation of processing temperature regardless of composite types (box part or panel). Cellular structure changes in the box part were found considering near or far from injecting point.Microcellular injection‐moulded box part (geometry: 150 × 100 × 70 mm3 in size) of soft wood fibre–PP composites.magnified imageMicrocellular injection‐moulded box part (geometry: 150 × 100 × 70 mm3 in size) of soft wood fibre–PP composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have