Abstract
Reversible temper embrittlement has been frequently observed in many different low alloy steels serving at high temperature, e.g. order of 500 °C. This type of embrittlement can change the brittle transgranular fracture mode to intergranular decohesion with subsequent change in fracture stress and fracture toughness. The present paper deals with the influence of the prior austenite grain size and isothermal aging time on the degree of embrittlement of 2.25Cr-1Mo steel, which is very popular for its use in power generating and other petrochemical industries. In this research work, the specimens of 2.25Cr-1Mo steel were treated in three different austenitizing temperatures along with different isothermal embrittling time periods. Then the induced degree of embrittlement was characterized by the fracture stress values at −196 °C and area fraction of intergranular failure. The outcome of the experimental results shows that the increase in austenite grain size and/or isothermal embrittling time severely weakens the grain boundary cohesive strength leading to brittle intergranular failures and thus to a greater degree of temper embrittlement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.