Influence of precursor concentration on physical properties of CdO thin films prepared by spray pyrolysis technique using nebulizer

Abstract

Cadmium oxide (CdO) thin films were prepared with different concentrations of precursor solution (0.05, 0.1, 0.15, 0.2 and 0.25 M, respectively) at the optimized temperature (200 °C) using the nebulized spray pyrolysis technique to obtain better crystallinity in polycrystalline thin films on amorphous glass substrates. The XRD characterization of those samples revealed a preferential orientation along the (111) plane having a cubic structure. The scanning electron microscopy (SEM) analysis displayed that all the as-deposited thin films have spherical shaped grains. The transmittance of the as-deposited CdO thin films had decreased from 88 to 71% for longer wavelength regions (600–900 nm) as the precursor concentration had increased and then increased for higher precursor concentration. The optical band gap was found to lie between 2.45 and 2.40 eV belonging to direct transition for those thin films. The presence of Cd–O bond (540 cm−1) was confirmed by FTIR spectrum. The emission properties of CdO thin films were studied by luminescence spectrum recorded at room temperature. A maximum carrier concentration and minimum resistivity values of 4.743 × 1019 cm− 3 and 1.06 × 10−3 Ω-cm, respectively, were obtained for 0.2 M precursor concentration. These CdO thin films have high optical transmittance and high room temperature conductivity, which can be used as the TCO and Solar cell (window layer) material.