Abstract
Abstract Metal matrix composite (MMC) clads were developed through microwave cladding technique on CA6NM substrate using different microwave power levels. The influence of microwave power was investigated on the microstructure, phase evolution, mechanical properties, and erosion-tribo performance of the clad layers. Increase in microwave power resulted in reduction of Cr7C3 phase in clad layers, which eventually decreases the fracture toughness and microhardness of the clad. Clad fabricated at 600 W exhibited highest fracture toughness (11.6 ± 0.58 MPa√m) and microhardness (949 ± 47.45 HV). All clads exhibited highest erosion at 60 deg indicating a mixed erosion mode. Clads fabricated at power levels beyond 600 W, with less Cr7C3 content exhibited severe carbide pullout, thus deteriorated the slurry erosion resistance of the clads.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.