Abstract
The effect of potassium pyrophosphate in the electrolyte on plasma electrolytic oxidation (PEO) process for AZ91 Mg alloy was investigated. The morphologies and chemical compositions of the coating layer on the AZ91 Mg alloy were evaluated and corrosion resistance was also estimated by potentiodynamic polarization analysis. The coating layer on AZ91 Mg alloy coated from the Bath 2 containing 0.03 mol/L of potassium pyrophosphate for 360 s exhibited considerably dense structure and contained 11%–18% (mass fraction) of phosphorous. The higher content of phosphorous of coating layer coated from Bath 2 could be detected at the bottom of oxide layer, which strongly implied that the phosphorous ion might be concentrated at the barrier layer. Corrosion potential of coating layer of AZ91 Mg alloy increased and corrosion current density decreased with increasing the concentration of potassium pyrophosphate. The polarization resistance ( R p) of coating layer of AZ91 Mg alloy coated from Bath 2 was 4.65×10 7 Ω/cm 2, which was higher than that ( R p=3.56×10 4 Ω/cm 2) of the sample coated from electrolyte without potassium pyrophosphate. The coating layer coated from Bath 2 containing 0.03 mol/L potassium pyrophosphate exhibited the best corrosion resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.