Influence of postprocessing rinsing solutions and duration on flexural strength of aged and nonaged additively manufactured interim dental material

Abstract

Statement of problemAdditive manufacturing procedures for fabricating interim restorations include rinsing postprocessing procedures. However, the impact of different rinsing solutions and times on flexural strength is unknown. PurposeThe purpose of this in vitro study was to assess the influence of the rinsing solutions and duration, as well as accelerated aging (thermocycling) procedures, on the flexural strength and Weibull characteristics of an additively manufactured interim dental material. Material and methodsA bar design (25×2×2 mm) file was used to fabricate all the specimens with 3D printing and an interim material (Nextdent C&B MFH). Five groups were created based on the rinsing solution used during the postprocessing procedures: 91% isopropyl alcohol (IPA) (control or IPA-91), 99% IPA (IPA-99 group), bio-ethyl alcohol 100% (BE group), tripropylene glycol monomethyl ether (TPM) 100% (TPM group), and water miscible formula (Resinaway) (RA group). Each group was divided into 4 subgroups depending on the total rinsing time: 5, 6, 7, and 8 minutes (5, 6, 7, and 8 subgroups). Additionally, each subgroup was distributed between nonaged and aged thermocycling procedures (n=10). Flexural strength measurements were made by using a universal testing machine. Two-parameter Weibull distribution values, including the Weibull modulus, scale (m), and shape (0), were calculated. Three-way ANOVA and pairwise multiple comparison Tukey tests were used to analyze the data (α=.05). ResultsThree-way ANOVA showed that the rinsing solution (P<.001), rinsing time (P=.004), and thermocycling procedures (P<.001) were significant predictors of the flexural strength values obtained. The IPA-91 and IPA-99 groups obtained the highest flexural strength, while the RA, TPM, and BE groups obtained the lowest flexural strength. The 7- and 8-minute subgroups obtained the highest flexural strength, while the 5-minute subgroup obtained the lowest flexural strength. The nonaged specimens obtained significantly higher mean flexural strength values than the aged specimens. ConclusionsThe vat-polymerized additively manufactured interim dental material tested with differing rinsing solutions and times demonstrated significant differences in the flexural strength values measured. Accelerated artificial aging procedures significantly decreased the flexural strength of the vat-polymerized interim dental material tested.