Influence of polymeric electron injection layers on the electrical properties of solution-processed multilayered polymer light-emitting diodes

Abstract

In this study, we fabricated multilayered polymer-based light-emitting diodes (pLEDs) with various solution-processed electron-injection layers (EILs), and investigated the influence of the EILs on the electrical properties of pLEDs in indium tin oxide (ITO)/poly(3,4-ethylenedioxythiophene) doped with poly(styrene sulfonic acid) (PEDOT:PSS)/poly[(9,9-dioctylfluorene-alt-(1,4-phenylene((4-sec-butylphenyl)amino)-1,4-phenylene))] (TFB) (HTL)/poly(9,9-dioctylfluorene-alt-1,4-benzothiadiazole) (F8BT) (EML)/EIL/Al structures. We have used the quaternized ammonium π-conjugated polyelectrolyte derivative (poly[(9,9-di(3,3′-N,N′-trimethylammonium)propylfluorenyl-2,7-diyl)-co-(1,4-phenylene)]diiodide salt) (PF–PDTA), a mixture of PF–PDTA and CS2CO3, and the aliphatic-amine-based polymer poly(ethylene imine) (PEI) as solution-processed EILs, and compared them with LiF as a solvent-free EIL. The EILs enhanced the electron injection and improve the pLED performance. High external quantum efficiencies of nearly 4% were obtained in the pLEDs with the combination of a multilayered structure fabricated by a transfer printing technique and EILs of a PF–PDTA:CS2CO3 mixture and PEI. On the other hand, the device with PF–PDTA exhibited lower efficiency, higher driving voltage, and larger leakage current at lower voltage. The migration of ionic charges was suggested from the abnormal dielectric behaviors, and serious damage on the electrode material occurred when both an acid hole-injection layer (PEDOT:PSS) and PF–PDTA were used. On the other hand, the pLEDs with ultrathin PEI showed high performance and stable device operation in terms of the influence of ionic charges.