Potassium fluorophlogopite glass ceramics were prepared. Differential thermal analysis showed that there were two exothermic peaks at ∼750 and 950°C, corresponding to the Avrami exponent ∼1·5 and 2·0. Spherical particles were found using a scanning electron microscope when the glass ceramics were heat treated at 750 and 800°C. With the increase in heat treatment temperature, a kind of lamellar crystals was gradually formed, and the shape of crystals changed from spherical to lamellar when the Avrami exponent changed from 1·5 to 2·0. Mechanical tests showed that material cutting and bending strength increased, while the Vickers hardness decreased with the increasing of P2O5 content and heat treatment temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.