Abstract
Four-arm, star-shaped poly(D,L-lactide) (PDLLA) oligomers of controlled molar mass and narrow molar mass distribution were successfully synthesized by use of an ethoxylated pentaerythritol initiator. Derivatization of the terminal hydroxyl groups with either methacrylic anhydride (MAAH) or 2-isocyanatoethyl methacrylate (IEM) to yield PDLLA-M (M = methacrylate end group) and PDLLA-UM (UM = urethane methacrylate end group), respectively, was monitored by in situ Fourier transform infrared (FTIR) spectroscopy. Photo-cross-linking of the functional oligomers yielded networks with high gel contents (>95%). The glass transition temperature (T(g)) of these networks was strongly dependent on prepolymer molar mass, and networks based on low molar mass precursors were more rigid than the networks obtained from higher molar mass oligomers. The tensile strength (TS) and Young's modulus of the PDLLA-M samples, approximately 7 and 17 MPa, respectively, were significantly lower than the values of 19 MPa (TS) and 113-354 MPa (Young's modulus) for the PDLLA-UM samples. The introduction of terminal hydrogen-bonding sites that were adjacent to the photo-cross-linking site resulted in higher performance poly(lactide)-based bioadhesives.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.